Slider

http://3d.3dbiocadedu.com/wp-content/uploads/sites/10/2016/08/truzirht.jpg

TruZir High Translucency

TruZir High Translucency zirconia blocks are translucent and use a cold isostatic pressure process; therefore, the blank is more homogeneous then a uniaxial pressed blank, and the shrinkage factor is even throughout the blank. 3D BioCAD Zirconia blank has a high strength, excellent biocompatibility and aesthetics. High Translucency (HT) blocks are available in Size: 10, 12, 14, 16, 18, 20, 22, 25mm


Gallery

Arrow
Arrow
ArrowArrow

Slider


Specifications

Product TruZir High Translucency
Sintering temperature(oC) 1550
Bending Strength (Mpa) 1200
Sintering Density (g/m3) 6.05
Average Grain Size (um) 0.4
Amount of monoclinic phase after accelerated ageing (%) <10
Light transmittance 43% (sample thickness 1mm)
Radioactivity (Bq/g) <0.1

Additional Information

Recommended sintering schedule
R.T.~ 1000oC 100 min 10oC/min
1000oC ~ 1300oC 60 min 5oC/min
1300oC ~ 1550oC 100 min 2oC/min
1550oC 120 min holding Holding
1550oC ~ 900oC 120 min 5oC/min
900oC 30 min holding Holding
900oC ~ 700oC 20 min 10oC/min
700oC ~ R.T. 50 min 14oC/min
Faster Sintering Schedule
R.T.~ 1100oC 50 min 22oC/min
1100oC ~ 1550oC 100 min 5oC/min
1550oC 90 min holding Holding
1550oC ~ 700oC 60 min 14oC/min